XPS Spectra
Bromine (Br) Compounds
The XPS Spectra section provides raw and processed survey spectra, chemical state spectra, BE values, FWHM values, and overlays of key spectra.
Atom% values from surveys are based on sample, as received, and Scofield cross-sections. Atom% values are corrected for IMFP and PE.
Peak-fits are guides for practical, real-world applications. Peak-fits are not fully optimized or designed to test any theory.

---

Calcium Bromide  (CaBr₂)
Survey, Peak-fits, BEs, FWHMs, and Peak Labels

---

→  Periodic Table	→ Six (6) BE Tables
Survey Spectrum from CaBr2 Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag (3d5/2) FWHM = 1.3 eV
→  Periodic Table	→ Six (6) BE Tables
Br (3d) Spectrum from CaBr2 – Raw Fresh exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV	Br (3d) Spectrum from CaBr2 – Peak-Fit Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV
Br (3d) Spectrum from CaBr2 – Extended  Fresh exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV	Br (3d) Spectrum from CaBr2 – Raw – Expanded Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV
→  Periodic Table	→ Six (6) BE Tables
Ca (2p) Spectrum from CaBr2 – Raw Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV	Ca (2p) Spectrum from CaBr2 – Peak-Fit Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV
→  Periodic Table	→ Six (6) BE Tables
Ca (2p) Spectrum from CaBr2 – Raw – Extended  Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV	Ca (2p) Spectrum from CaBr2 – Raw – Expanded Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV
→  Periodic Table	→ Six (6) BE Tables
C (1s) Spectrum from CaBr2 – Raw Freshly exposed bulk, Flood gun is ON, C (1s) BE = 284.49 eV, Ag FWHM = 0.75 eV	C (1s) Spectrum from CaBr2 – Peak-Fit Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV

---

→  Periodic Table	→ Six (6) BE Tables
Ca (LMM) Auger Signals from CaBr2 – Raw Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV	Valence Band Signals from CaBr2 – Raw Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV

Overlays
→  Periodic Table	→ Six (6) BE Tables
Valence Band Spectra – Overlay of KBr and CaBr2 Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV	Br (3d) Spectra – Overlay of KBr and CaBr2 Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV
→  Periodic Table	→ Six (6) BE Tables
Valence Band Spectra – Overlay of xx and CaBr2 Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV	Br (3d) Spectra – Overlay of xxx and CaBr2 Freshly exposed bulk, Flood gun is ON, C (1s) BE = 285.0 eV, Ag FWHM = 0.75 eV
End-of-spectra Price to purchase raw data sets: Raw spectra – VAMAS ASCII format ($6) Raw spectra – SDP binary format ($5) SDP v9 – $145 (3 yr license)     Transmission Function Tests

December 2015 – Transmission Function of Thermo K-Alpha Plus

→  Periodic Table

Survey Spectra of Ion Etched Copper (Cu), PEs = 50, 100, 150 and 200 eV

→  Periodic Table

March 2016 – Transmission Function of Thermo K-Alpha Plus

Survey Spectra of Ion Etched Copper (Cu), PEs = 100, 150 and 200 eV

→  Periodic Table

August 2019 – Transmission Function of Thermo K-Alpha Plus

Survey Spectra of HOPG (C), PEs = 20, 50, 100 and 200 eV

→  Periodic Table

January 2022 – Transmission Function of Thermo K-Alpha Plus

Survey Spectra of Ion Etched Copper (Cu), PEs = 100, 120, 140, 160, 180 and 200 eV

---

---

 

Six (6) Chemical State Tables of Br (3d_5/2) BEs

 

• The XPS Library Spectra-Base
• PHI Handbook
• Thermo-Scientific Website
• XPSfitting Website
• Techdb Website
• NIST Website

 

---

---

 

Notes of Caution when using Published BEs and BE Tables from Insulators and Conductors:

• Accuracy of Published BEs
  • The accuracy depends on the calibration BEs used to calibrate the energy scale of the instrument.  Cu (2p_3/2) BE can vary from 932.2 to 932.8 eV for old publications
  • Different authors use different BEs for the C (1s) BE of the hydrocarbons found in adventitious carbon that appears on all materials and samples.  From 284.2 to 285.3 eV
  • The accuracy depends on when the authors last checked or adjusted their energy scale to produce the expected calibration BEs
• Worldwide Differences in Energy Scale Calibrations
  • For various reasons authors still use older energy scale calibrations
  • Some authors still adjust their energy scale so Cu (2p_3/2) appears at 932.2 eV or 932.8 eV because this is what the maker taught them
  • This range causes BEs in the higher BE end to be larger than expected
  • This variation increases significantly above 600 eV BE
• Charge Compensation
  • Samples that behave as true insulators normally require the use of a charge neutralizer (electron flood gun with or without Ar+ ions) so that the measured chemical state spectra can be produced without peak-shape distortions or sloping tails on the low BE side of the peak envelop.
  • Floating all samples (conductive, semi-conductive, and non-conductive) and always using the electron flood gun is considered to produce more reliable BEs and is recommended.
• Charge Referencing Methods for Insulators
  • Charge referencing is a common method, but it can produce results that are less reliable.
  • When an electron flood gun is used, the BE scale will usually shift to lower BE values by 0.01 to 5.0 eV depending on your voltage setting. Normally, to correct for this flood gun induced shift, the BE of the hydrocarbon C (1s) peak maximum from adventitious carbon is used to correct for the charge induced shift.
  • The hydrocarbon peak is normally the largest peak at the lowest BE.
  • Depending on your preference or training, the C (1s) BE assigned to this hydrocarbon peak varies from 284.8 to 285.0 eV.  Other BEs can be as low as 284.2 eV or as high as 285.3 eV
  • Native oxides that still show the pure metal can suffer differential charging that causes the C (1s) and the O (1s) and the Metal Oxide BE to be larger
  • When using the electron flood gun, the instrument operator should adjust the voltage and the XY position of the electron flood gun to produce peaks from a strong XPS signal (eg O (1s) or C (1s) having the most narrow FWHM and the lowest experimentally measured BE.

→  Periodic Table 

---

Table #1

Br (3d_5/2) Chemical State BEs from:  “The XPS Library Spectra-Base”

C (1s) BE = 285.0 eV for TXL BEs
and C (1s) BE = 284.8 eV for NIST BEs

Element	Atomic #	Compound	As-Measured by TXL or NIST Average BE	Largest BE	Hydrocarbon C (1s) BE	Source
Br	35	NH4-Br	68.2 eV		285.0 eV	The XPS Library
Br	35	CsBr	68.2 eV		285.0 eV	The XPS Library
Br	35	CsBr (N*3)	68.2 eV	68.3 eV	284.8 eV	Avg BE – NIST
Br	35	Br-Na (N*2)	68.7 ev	68.8 eV	284.8 eV	Avg BE – NIST
Br	35	KBr (N*4)	68.7 eV	68.9 eV	284.8 eV	Avg BE – NIST
Br	35	CuBr2 (N*2)	68.9 eV	69.6 eV	284.8 eV	Avg BE – NIST
Br	35	Na-Br	69.0 eV		285.0 eV	The XPS Library
Br	35	Li-Br	69.0 eV		285.0 eV	The XPS Library
Br	35	K-Br	69.0 eV		285.0 eV	The XPS Library
Br	35	Br-Li (N*1)	69.2 eV		284.8 eV	Avg BE – NIST
Br	35	Br3-styrene	70.7 eV		285.0 eV	The XPS Library

Charge Referencing

• (N*number) identifies the number of NIST BEs that were averaged to produce the BE in the middle column.
• Binding Energy Scale Calibration expects Cu (2p_3/2) BE = 932.62 eV and Au (4f_7/2) BE = 83.98 eV.  BE (eV) Uncertainty Range:  +/- 0.2 eV
• Charge Referencing of insulators is defined such that the Adventitious Hydrocarbon C (1s) BE (eV) = 285.0 eV.  NIST uses C (1s) BE = 284.8 eV 
• Note:   Ion etching removes adventitious carbon, implants Ar (+), changes conductivity of surface, and degrades chemistry of various chemical states.
• Note:  Ion Etching changes BE of C (1s) hydrocarbon peak.
• TXL – abbreviation for: “The XPS Library” (https://xpslibrary.com).  NIST:  National Institute for Science and Technology (in USA)

→  Periodic Table 

---

Table #2

Br (3d_5/2) Chemical State BEs from:  “PHI Handbook”

C (1s) BE = 284.8 eV

 

→  Periodic Table 

Copyright ©:  Ulvac-PHI

---

Table #3

Br (3d_5/2) Chemical State BEs from:  “Thermo-Scientific” Website

C (1s) BE = 284.8 eV

Chemical state	Binding energy Br (3d5/2) / eV
KBr	68.7

→  Periodic Table 

Copyright ©:  Thermo Scientific 

---

Table #4

Br (3d_5/2) Chemical State BEs from:  “XPSfitting” Website

Chemical State BE Table derived by Averaging BEs in the NIST XPS database of BEs
C (1s) BE = 284.8 eV

→  Periodic Table 

Copyright ©:  Mark Beisinger

---

Table #5

Br (3d_5/2) Chemical State BEs from:  “Techdb.podzone.net” Website

 

XPS Spectra – Chemical Shift | Binding Energy
C (1s) BE = 284.6 eV

XPS(X線光電子分光法)スペクトル 化学状態 化学シフト ケミカルシフト

Element	Level	Compound	B.E.(eV)		min		max
Br	3d5/2	CsBr	68.3	±0.2	68.1	～	68.4
Br	3d5/2	RbBr	68.5	±0.2	68.3	～	68.7
Br	3d5/2	Pt(NH3)4Br2	68.5	±0.2	68.3	～	68.7
Br	3d5/2	KBr	68.8	±0.3	68.5	～	69.0
Br	3d5/2	NaBr	68.8	±0.3	68.5	～	69.0
Br	3d5/2	PbBr2	68.8	±0.3	68.5	～	69.0
Br	3d5/2	Ni(NH3)6Br2	68.8	±0.3	68.5	～	69.0
Br	3d5/2	CuBr2	69.1	±0.3	68.8	～	69.3
Br	3d5/2	LiBr	69.2	±0.3	68.9	～	69.4
Br	3d5/2	K2PtBr6	69.2	±0.3	68.9	～	69.5
Br	3d5/2	K2PtBr4	69.3	±0.3	69.0	～	69.5

 

→  Periodic Table 

---

---

 

Histograms of NIST BEs for Br (3d_5/2) BEs

Important Note:  NIST Database defines Adventitious Hydrocarbon C (1s) BE = 284.8 eV for all insulators.

Histogram indicates:  68.8 eV for Br- in KBr based on 4 literature BEs	Histogram indicates xxx

Table #6

NIST Database of Br (3d_5/2) Binding Energies

NIST Standard Reference Database 20, Version 4.1

Data compiled and evaluated
by
Alexander V. Naumkin, Anna Kraut-Vass, Stephen W. Gaarenstroom, and Cedric J. Powell
©2012 copyright by the U.S. Secretary of Commerce on behalf of the United States of America. All rights reserved.

Important Note:  NIST Database defines Adventitious Hydrocarbon C (1s) BE = 284.8 eV for all insulators.

→  Periodic Table 

---

 

 

Statistical Analysis of Binding Energies in NIST XPS Database of BEs

 

 

→  Periodic Table 

 

---

---